Refractory Cement CA80

Catalog: Refractory Cement | 2021-12-30

1. Model: CA75, CA80, CA80S
2. Material: Calcium aluminate

√ Good fluidity
√ High refractoriness
√ Excellent mechanical performance

Product Details

KERUI produces high purity Calcium Aluminate Cements with 70, 75 and 80% Al2O3 content by sintering process.

These products not only widely used throughout the refractory industry, but also in other areas such as building chemistry materials are in high demand. 

【Description】

As a high purity product, CA80 contains approximately 80% of alumina, the specific properties of CA80 give high performance concretes the following properties, high refractoriness, excellent mechanical performance.

So it can be used in the refractory industry in conventional and low cement castables, which require fast setting, high early strength development, and good strength at intermediate temperatures. And the very high purity level of CA80 makes it suitable for certain refractory applications. For example: in reducing atmospheres where hydrogen or carbon monoxide is present, low silica and iron oxide are vital.

11.jpg22.jpg

The 80% alumina cements of KERUI are represented by two product types, CA80 and CA80S.

”CA80S has good fluidity, long workable time and low water demand, ideal to produce castables of good working ability and excellent mechanical strength property without any additives, also it suits very well to be used in high temperature environment or hot summer time.“

Notes: refractory cement = high alumina cement = Calcium aluminate cement

ProductsCA75CA75CA80CA80CA80SCA80S
Workable timeModerateModerateShortShortLongerLonger
StandardUsual rangeSpecification limitUsual rangeSpecification limitUsual rangeSpecification limit
SiO2, %0.1-0.4≤0.50.1-0.4≤0.50.1-0.4≤0.5
Al2O3, %73.5-75.5≥7378.0-80.0≥7778.0-80.0≥77
Fe2O3, %0.1-0.4≤0.50.1-0.4≤0.50.1-0.4≤0.5
CaO, %21.0-23.0-18.5-20.5-18.5-20.5-
R2O, %-≤0.4-≤0.4-≤0.4
S-, %-≤0.1-≤0.1-≤0.1
CI-, %-≤0.06-≤0.06-≤0.06
d50(μm)6-9≤105-8≤95-8≤9
325M(%)-≤5.0-≤5.0-≤5.0
Specific surface areas(㎡/kg)420-480≥400450-500≥450450-500≥450
Setting time, min





Initial setting time IS150-200≥150150-210≥30210-270≥180
Final setting time FS240-300≤360210-270≤300260-320≤360
Flexural strength, Mpa





1d6.5-8.5≥4.06.0-8.0≥4.05.5-7.5≥4.0
3d8.5-10.5≥5.07.0-9.0≥5.07.0-9.0≥5.0
Compressive strength, Mpa





1d42-52≥2540-50≥2535-45≥25
3d52-62≥3050-60≥3050-60≥30


【Additional Information】

Principal phase: CA, CA2, Aα

Secondary phase: C12A7

Pyrometric cone equivalent: 1750-1800℃

Bulk density: 800-900 kg/m3

Specific gravity: 3.1-3.2 g/cm3

Shelf Life: 6 months

【Packaging and Storage】

Packing method: Standard export packaging

Paper bags: 25/50kg

Big bags: 1.0/1.5mt

Storage tips:High purity calcium aluminate cements must be stored in dry conditions, off the ground. In this case, it will retain its proper ties for at least 6 months. In many instances, experience has demonstrated that properties are retained for more than one year.